Metallurgical failure mode of cracking under a prolonged static load
Sustained load cracking, or SLC, is a metallurgical phenomenon that occasionally develops in pressure vessels and structural components under stress for sustained periods of time.[1]
It is particularly noted in aluminium pressure vessels such as diving cylinders.[2][3]
Sustained load cracking is not a manufacturing defect; it is a phenomenon associated with certain alloys and service conditions:
- 6351 aluminum alloy[2]
- Overstressing due to excessive filling pressure[2]
- Abuse and mechanical damage[2]
Occurrence
Crack growth is reported to be very slow by Luxfer, a major manufacturer of aluminium high-pressure cylinders.[4] Cracks are reported to develop over periods in the order of 8 or more years before reaching a stage where the cylinder is likely to leak, which allows timely detection by properly trained inspectors using eddy-current crack-detection equipment.[5]
SLC cracks have been detected in cylinders produced by several manufacturers, including Luxfer, Walter Kidde, and CIG gas cylinders.
Most of the cracking has been observed in the neck and shoulder areas of cylinders, though some cracks in the cylindrical part have also been reported.[1]
History
The phenomenon was first noticed in 1983 in hoop-wound fibre-reinforced aluminium alloy cylinders, which burst in use in the USA. The alloy was 6351 with a relatively high lead content (400 ppm), but even after the lead content was lowered, the problem recurred, and subsequently the problem was detected in monolithic aluminium cylinders.[6][5] The first incidence of an SLC crack in the cylindrical part of a cylinder was reported in 1999.[1]
Detection
Neck cracks are readily observed during inspection, but body and shoulder cracks are more difficult to detect.[1] Neck thread cracks can be non-destructively tested using eddy-current crack-detection equipment. This is reported to be reliable for alloy 6351, but false positives have been reported for tests on alloy 6061.[5]
Contributing factors
All of these forms of crack development are the result of the cylinder being subject to high pressure for prolonged periods. The cracks are intergranular and occur at grain boundaries. There is no evidence of stress corrosion or fatigue.[1][5]
The presence of a relatively high lead content has been identified as a contributory factor. Cracking at the grain boundaries is accelerated in the presence of lead. The presence of bismuth is also suspected to be contributory.[1]
Alloy composition has also been found to be a factor. Alloy 6061 has shown good resistance to SLC, as have alloys 5283 and 7060. Manufacturing defects such as folds on the inside surface have been shown to be harmful, particularly for parallel-threaded cylinders. Grain size has been shown to be of relatively minor importance.[1][5]
Alloy composition
Material Code[1] Element (wt. %) | Alloy 6082† | Alloy 6351† | Alloy 6061 | Alloy 5283 | Alloy 7060 |
Silicon | 0.7–1.3 | 0.7–1.3 | 0.4–0.8 | Max 0.30 | Max 0.15 |
Iron | Max 0.50 | Max 0.50 | Max 0.70 | Max 0.30 | Max 0.20 |
Copper | Max 0.10 | Max 0.10 | 0.15–0.40 | Max 0.03 | 1.8–2.6 |
Manganese | 0.40–1.0 | 0.40–0.80 | Max 0.15 | 0.5–1.0 | Max 0.20 |
Magnesium | 0.6–1.2 | 0.40–0.80 | 0.8–1.2 | 4.5–5.1 | 1.3–2.1 |
Chromium | Max 0.25 | - | 0.04–0.35 | Max 0.05 | 0.15–0.25 |
Zinc | Max 0.20 | Max 0.20 | Max 0.25 | Max 0.10 | 6.1–7.5 |
Titanium | Max 0.10 | Max 0.20 | Max 0.15 | Max 0.03 | Max 0.05 |
Others each* | Max 0.05 | Max 0.05 | Max 0.05 | Max 0.05 | Max 0.05 |
Others total | Max 0.15 | Max 0.15 | Max 0.15 | Max 0.15 | Max 0.15 |
Aluminium | Remainder | Remainder | Remainder | Remainder | Remainder |
*In addition to this limit it is necessary to restrict lead and bismuth to 0.003% max. † Alloy 6351 is essentially within the limit of alloy 6082. |
See also
- Underwater diving portal
References
- ^ a b c d e f g h Barthélémy, Hervé; Birch, David; Dörner, Wolfgang; Erlandsson, Jörgen; Gabrieli, Giorgio; Kriese, Alexander; Vandererven, Els; Webb, Andy (2004). Recommendations for avoidance of sustained load cracking of aluminium alloy cylinders, IGC Doc 57/11/E, Revision of IGC Doc 57/04/E. Brussels: European Industrial Gases Association AISBL. Retrieved 1 September 2012.
- ^ a b c d Luxfer Gas Cylinders (2015). "Sustained-load cracking - which types of cylinders are most susceptible to SLC-related ruptures?". Luxfer Gas Cylinders. Retrieved 6 October 2018.
- ^ High, Bill. "Cracking and Ruptures of SCBA and SCUBA Aluminum Cylinders Made from 6351 Alloy (Archived copy)" (PDF). PSI, Inc. Archived from the original (PDF) on 2015-12-26. Retrieved 2015-10-09. originally accessed 30 August 2012.
- ^ Luxfer Gas Cylinders (2015). "Sustained-load cracking - how quickly do the cracks grow?". Luxfer Gas Cylinders. Retrieved 6 October 2018.
- ^ a b c d e "Sustained-load cracking (SLC) in ruptured scuba cylinder made from 6351 aluminum alloy (Archived copy)". 22 October 2007. Archived from the original on 2015-06-17. Retrieved 2015-10-09.
- ^ Solid forgings, without filament wound reinforcement.
Underwater diving
- Diving activities
- Diving modes
- Atmospheric pressure diving
- Freediving
- Saturation diving
- Scuba diving
- Snorkeling
- Surface oriented diving
- Surface-supplied diving
- Unmanned diving
|
Diving equipment |
---|
Basic equipment | - Diving mask
- Snorkel
- Swimfin
|
---|
Breathing gas | |
---|
Buoyancy and trim equipment | |
---|
Decompression equipment | |
---|
Diving suit | |
---|
Helmets and masks | |
---|
Instrumentation | |
---|
Mobility equipment | |
---|
Safety equipment | |
---|
Underwater breathing apparatus | |
---|
Diving equipment manufacturers | |
---|
|
|
|
---|
Access equipment | |
---|
Breathing gas handling | |
---|
Decompression equipment | |
---|
Platforms | |
---|
Remotely operated underwater vehicles | |
---|
Safety equipment | |
---|
General | |
---|
|
|
|
---|
Activities | |
---|
Competitions | |
---|
Equipment | |
---|
Freedivers | |
---|
Hazards | |
---|
Historical | |
---|
Organisations | |
---|
|
|
|
---|
Occupations | |
---|
Underwater work | Salvage diving | - SS Egypt
- Kronan
- La Belle
- SS Laurentic
- RMS Lusitania
- Mars
- Mary Rose
- USS Monitor
- HMS Royal George
- Vasa
|
---|
|
---|
Diving contractors | |
---|
Tools and equipment | |
---|
Underwater weapons | |
---|
|
|
|
---|
Specialties | |
---|
Diver organisations | |
---|
Diving tourism industry | |
---|
Diving events and festivals | |
---|
|
|
|
---|
Diving hazards | |
---|
Diving procedures | |
---|
Risk management | |
---|
|
|
|
---|
Diving disorders | Pressure related | Oxygen | |
---|
Inert gases | |
---|
Carbon dioxide | |
---|
Breathing gas contaminants | |
---|
|
---|
Immersion related | |
---|
|
---|
Treatment | |
---|
Personnel | |
---|
Screening | |
---|
Research | Researchers in diving physiology and medicine | |
---|
Diving medical research organisations | |
---|
|
---|
|
|
|
|
---|
Archeological sites | |
---|
Underwater art and artists | |
---|
Engineers and inventors | |
---|
Historical equipment | |
---|
Military and covert operations | - Raid on Alexandria (1941)
- Sinking of the Rainbow Warrior
|
---|
Scientific projects | |
---|
Awards and events | |
---|
Incidents | Dive boat incidents | |
---|
Diver rescues | |
---|
Early diving | |
---|
Freediving fatalities | |
---|
Offshore diving incidents | - Byford Dolphin diving bell accident
- Drill Master diving accident
- Star Canopus diving accident
- Stena Seaspread diving accident
- Venture One diving accident
- Waage Drill II diving accident
- Wildrake diving accident
|
---|
Professional diving fatalities | |
---|
Scuba diving fatalities | |
---|
|
---|
|
|
Publications |
---|
Manuals | - NOAA Diving Manual
- U.S. Navy Diving Manual
- Basic Cave Diving: A Blueprint for Survival
- Underwater Handbook
- Bennett and Elliott's physiology and medicine of diving
- Encyclopedia of Recreational Diving
- The new science of skin and scuba diving
- Professional Diver's Handbook
- Basic Scuba
|
---|
Standards and Codes of Practice | |
---|
General non-fiction | |
---|
Research | |
---|
Dive guides | |
---|
|
|
Training and registration |
---|
Diver training | |
---|
Recreational scuba certification levels | Core diving skills | |
---|
Leadership skills | |
---|
Specialist skills | |
---|
|
---|
Diver training certification and registration organisations | Commercial diver certification authorities | |
---|
Commercial diving schools | |
---|
Free-diving certification agencies | |
---|
Recreational scuba certification agencies | |
---|
Scientific diver certification authorities | |
---|
Technical diver certification agencies | |
---|
|
---|
Military diver training centres | |
---|
Military diver training courses | |
---|
|
|
|
---|
Surface snorkeling | |
---|
Snorkeling/breath-hold | |
---|
Breath-hold | |
---|
Open Circuit Scuba | |
---|
Rebreather | |
---|
Sports governing organisations and federations | |
---|
Competitions | |
---|
|
|
|
---|
Pioneers of diving | |
---|
Underwater scientists archaeologists and environmentalists | |
---|
Scuba record holders | |
---|
Underwater filmmakers and presenters | |
---|
Underwater photographers | |
---|
Underwater explorers | |
---|
Aquanauts | |
---|
Writers and journalists | |
---|
Rescuers | |
---|
Frogmen | |
---|
Commercial salvors | |
---|
|
|
|
---|
Diving physics | |
---|
Diving physiology | |
---|
Diving environment | |
---|
|
|
Other |
---|
Deep-submergence vehicle | - Aluminaut
- DSV Alvin
- American submarine NR-1
- Bathyscaphe
- Archimède
- FNRS-2
- FNRS-3
- Harmony class bathyscaphe
- Sea Pole-class bathyscaphe
- Trieste II
- Deepsea Challenger
- Ictineu 3
- JAGO
- Jiaolong
- Konsul-class submersible
- Limiting Factor
- Russian submarine Losharik
- Mir
- Nautile
- Pisces-class deep submergence vehicle
- DSV Sea Cliff
- DSV Shinkai
- DSV Shinkai 2000
- DSV Shinkai 6500
- DSV Turtle
- DSV-5 Nemo
|
---|
Submarine rescue | Deep-submergence rescue vehicle | |
---|
|
---|
Submarine escape | |
---|
Special interest groups | |
---|
Neutral buoyancy facilities for Astronaut training | |
---|
Other | |
---|
|
|
|